  • Product Name: Monosil Silane Cross-linked Polyethylene Compounds for Cable 10KV or Lower
  • Product Model:
  • Views :

immediate inquiry

XLPE Cable Compound, based On PE, is made into chemical XLPE insulating compound by plastic granulation with adding cross-linking agent and etc. the product has following characteristics: the melt pressure fluctuation is small while extrusion, load is moderate, not easy to be pre-crosslinked and burned; the surface of the extruded insulation layer is smooth ,round, good plasticizing properties.

 

 

Sample Model
And specification
YJG-10 Report No. CT16-6907
Sample Name Silane crosslinked polyethylene insulation material for XLPE insulated cable under 10kV
 No.   Test Item Unit

Technical 

Requirement

Test 

Result

Single 

Judgment

  Sample Color for test      White      N
1 Tensile Strength MPa  No less than 13.5 26.8 P
2 Elongation at break %  No less than 350 592 P
3

Low temperature impact brittleness 

temperature(-76℃)-Fracture 

number/ Style number

Piece No more than 15/30 0/30 P
4 Air high temperature aging
(135℃,168h)
       
4.1 Change rate of tensile strength % No more than ±20 -1.1 P
4.2

Change rate of Elongation

at break

% No more than ±20 -9.1 p
5 Thermal elongation
(200℃,0.2MPa,15Min)
       
5.1 Elongation rate under load % No more than 100 65 P
5.2

Permanent deformation 

after cooling

% No more than 100 65 p
6 Gelatum content % No less than 60 62 P
7

Dielectric loss factor

(50Hz,20℃)

  No more than1X10-3 5X10-4 P
8

Relative dielectric constant

(50Hz, 20℃)

  No more than 2.35 2.34 P
9 Volume resistivity (20℃) Ω.m No less than 1X1014 9X1014 P
10 Dielectric strength MV/m  No less than 25 37 P